Method for manufacturing capacitor in semiconductor device and the capacitor

ABSTRACT

In the method for manufacturing a capacitor in a semiconductor device, a nitride film is formed over a lower electrode on a semiconductor substrate, and a TaON film is formed over the nitride film. The Al 2 O 3  film is formed over the TaON film, and an upper electrode is formed over the Al 2 O 3  film.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The invention relates to a method for manufacturing a capacitor in a semiconductor device and the capacitor.

2. Description of the Related Art

Recently, the need for memory elements has increased with developments of techniques for manufacturing semiconductor devices. In a semiconductor device, a capacitor is used as a means for storing data. The capacitance of such a capacitor depends on the electrode area and the dielectric constant of a dielectric film interposed between electrodes of the capacitor.

However, as semiconductor devices become more highly integrated, the capacitor area given in the semiconductor device is reduced. Accordingly, the electrode area of the capacitor decreases, thereby causing a reduction in the capacitance of the capacitor.

In order to solve this problem, a capacitor comprising a TaON thin film of a high dielectric constant has been proposed, in which the TaON film has a metal film-insulating film-silicon (MIS) structure. An upper electrode over the TaON thin film is formed using a laminated structure composed of a polysilicon film deposited on a TiN film in order to enhance interface characteristics.

FIG. 1 is a cross-sectional view illustrating a conventional method for manufacturing a capacitor with a TaON thin film in a semiconductor device. As shown in FIG. 1, according to the conventional capacitor manufacturing method, a TaON thin film 2 having a high dielectric constant is deposited over a lower electrode 1, for example, a polysilicon film.

Then, a TiN/polysilicon film 3 having a laminated structure is deposited over the TaON thin film 2. The deposition of the TiN/polysilicon film 3 is achieved by forming a TiN thin film in a CVD (Chemical vapor Deposition) chamber using TiCl₄ as a precursor and NH₃ as a reaction gas. Thus, a capacitor with an MIS structure is completely formed.

However, there are some problems involved in the conventional method for manufacturing such a capacitor of a semiconductor memory device.

For example, as semiconductor devices become more highly integrated, the cell size is reduced, even though the capacitance per cell requisite for stably driving the device does not vary. Therefore, the TaON thin film having a single layer structure cannot assure a high enough capacitance of the capacitor and suppression of leakage current at the same time.

Also, after the deposition of the TaON thin film as a dielectric film and before the formation of the polysilicon film as an upper electrode, the formation of a TiN thin film has to be carried out in the CVD chamber using TiCl₄ as a precursor and NH₃ as a reaction gas in order to enhance the interface characteristics of the TaON thin film and the polysilicon film. Accordingly, there is an increase in the manufacturing costs for the additional process.

SUMMARY OF THE INVENTION

Therefore, the present invention has been made in order to solve the above-mentioned problems in the related art. An object of the present invention is to provide a capacitor and a method for manufacturing a capacitor in a semiconductor device, which is capable of achieving an improvement in the interface characteristics while assuring a high capacitance and a low leakage current.

In accordance with one aspect, the present invention provides a method for manufacturing a capacitor in a semiconductor device, comprising: forming a nitride film over a lower electrode, which is on a semiconductor substrate; forming a TaON film over the nitride film; forming an Al₂O₃ film over the TaON film; and forming an upper electrode over the Al₂O₃ film.

In accordance with another aspect, the present invention provides a method for manufacturing a capacitor in a semiconductor device, comprising: forming a nitride film over the lower electrode, which is on a semiconductor substrate, by using plasma; forming an amorphous TaON thin film over the nitride film; subjecting the amorphous TaON thin film to an RTA (Rapid Thermal annealing) treatment; forming an Al₂O₃ film over the amorphous TaON thin film; subjecting the Al₂O₃ film to a furnace vacuum thermal treatment; and forming a polysilicon film over the Al₂O₃ film to form an upper electrode.

In accordance with yet another aspect, the present invention provides a capacitor comprising: a lower electrode; a nitride film formed on the lower electrode; a TaON film formed over the nitride film; an Al₂O₃ film formed over the TaON film; and an upper electrode formed on the Al₂O₃ film film.

BRIEF DESCRIPTION OF THE DRAWINGS

The above objects, and other features and advantages of the present invention will become more apparent after a reading of the following detailed description when taken in conjunction with the drawings, in which:

FIGS. 1 is a cross-sectional view illustrating the method for manufacturing a capacitor in a semiconductor device in the prior art; and

FIGS. 2A to 2D are cross-sectional views respectively illustrating sequential processing steps of a method for manufacturing a capacitor in a semiconductor device according to the present invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Now, a preferred embodiment according to the present invention will be described in detail, with reference to the annexed drawings.

According to the present invention, as shown in FIG. 2A, a polysilicon film 10 is deposited as a lower electrode on a semiconductor substrate (not shown). The polysilicon film 10 is etched using HF or BOE (Buffer Oxide Etchant) to remove a natural oxide film formed on the surface thereof (not shown).

Then, a nitride film 20 is formed over the polysilicon film 10, in accordance with a plasma treatment using NH₃. The formation of the nitride film 20 over the polysilicon film 10, that is, the lower electrode, is carried out by conducting a plasma treatment in a chamber, kept at a pressure of 0.1 torr to 1.2 torr and a low substrate temperature of 300° C. to 500° C. for 10 to 600 seconds while supplying NH₃ gas in an amount of about 10 to 500 sccm and applying an RF power of 10 to 500 watt, thereby forming a nitride film.

As shown in FIG. 2B, an amorphous TaON thin film 30 having a high dielectric constant is formed over the nitride film 20. Preferably, the formation of the amorphous TaON thin film 30 is carried out according to a PECVD (Plasma Enhanced Chemical Vapor Deposition) process. More particularly, the amorphous TaON film 30 is formed by evaporating 0.001 cc to 2 cc of tantalum ethylate (Ta(OC₂H₅)₅) as a raw material in a vaporizer, kept at 170° C. to 190° C., thereby producing Ta chemical vapor, and supplying the Ta chemical vapor to the PECVD chamber, to which NH₃ gas is supplied in a flow rate of 10 to 500 sccm, while maintaining the PECVD chamber at a low pressure of 0.1 torr to 1.2 torr and a temperature of 300° C. to 500° C. and applying an RF power of 10 to 500 watt.

Subsequently, the amorphous TaON thin film 30 is subjected to a thermal treatment in order to increase the proportion of nitrides in the TaON thin film. As the thermal treatment, an RTP (Rapid Thermal Processing) treatment is carried out for an annealing period of 60 to 180 seconds at a temperature 700° C. to 850° C. in a chamber supplied with NH₃ gas in a flow rate of 1 to 10 slm.

As shown in FIG. 2C, an Al₂O₃ film 40 is then deposited over the TaON thin film 30 resulting from the above thermal treatment to form a dielectric film 50 having a double-layer structure. The deposition of the Al₂O₃ film 40 is carried out by depositing an Al₂O₃ film using a raw material of (CH₃)₃Al as a precursor in a chamber, kept at a temperature of 200° C. to 450° C. and a pressure of 0.1 torr to 1 torr while supplying H₂O gas. Thus, the dielectric film 50 is formed to have a laminated structure composed of the TaON thin film 30 and the Al₂O₃ film 40.

The dielectric film 50 is then subjected to a furnace vacuum thermal treatment in order to remove impurities and to prevent a crystallization and a loss of nitrides in the TaON thin film 40. The furnace vacuum thermal treatment of the dielectric film 50 is carried out using N₂ gas under the processing conditions of an annealing period of 5 to 60 minutes and a temperature or 600° C. to 850° C.

Finally, as shown in FIG. 2D, a polysilicon film 60 for an upper electrode is deposited over the dielectric film 50. Preferably, the polysilicon film 60 is deposited to a thickness of about 1,000 Å.

The lower electrode may have various structures, for example, a cylindrical structure or a stacked structure. Further, it may have a metal-in structure.

As described above, the method for manufacturing a capacitor of a semiconductor device according to the present invention has effects as follows.

In accordance with the present invention, the dielectric film has a double-layer structure composed of the TaON thin film and the Al₂O₃ film to assure a high capacitance and a low leakage current, as compared to the conventional dielectric film having a single layer structure. It is also possible to achieve an improvement in interface characteristics. Such an improvement in interface characteristics makes it possible to omit the deposition of the TiN film, which is involved in the conventional capacitor manufacturing method to improve the interface characteristics between the TaON thin film and the upper electrode. Thus, it is possible to simplify the entire process.

In addition, as semiconductor memory devices with improved characteristics can be formed, it is possible to achieve an increase in productivity.

Although the preferred embodiments of the invention have been disclosed for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims. 

What is claimed:
 1. A method for manufacturing a capacitor in a semiconductor device, comprising: forming a nitride film over a lower electrode, which is on a semiconductor substrate; forming a TaON film over the nitride film; forming an Al₂O₃ film over the TaON film; and forming an upper electrode over the Al₂O₃ film.
 2. The method according to claim 1, further comprising: thermally treating the TaON film prior to forming the Al₂O₃ film.
 3. The method according to claim 2, wherein the thermally treating step is a rapid thermal process.
 4. The method according to claim 2, further comprising: thermally treating the Al₂O₃ film prior to the forming an upper electrode step.
 5. The method according to claim 1, further comprising: thermally treating the Al₂O₃ film prior to the forming an upper electrode step.
 6. The method according to claim 5, where the thermally treating step is a furnace vacuum thermal treatment.
 7. The method according to claim 1, wherein the TaON film is an amorphous TaON thin film.
 8. The method according to claim 1, wherein the lower electrode has one of a cylindrical structure and a stacked structure.
 9. The method according to claim 1, wherein the forming the nitride film step forms the nitrude film over the lower electrode by conducting a plasma treatment in a chamber, kept at a pressure of 0.1 torr to 1.2 torr and a semiconductor substrate temperature of 300° C. to 500° C. for 10 to 600 seconds while supplying NH₃ gas in an amount of 10 to 500 sccm and applying an RF power of 10 to 500 watts.
 10. The method according to claim 1, wherein the forming the TaON film step forms an amorphous TaON thin film according to a PECVD (Plasma Enhanced Chemical Vapor Deposition) process by evaporating 0.001 cc to 2 cc of tantalum ethylate (Ta(OC₂H₅)₅) as a raw material in a vaporizer, kept at 170° C. to 190° C., to produce Ta chemical vapor, and supplying the Ta chemical vapor to the PECVD chamber, to which NH₃ gas is supplied in a flow rate of 10 to 500 sccm, while maintaining the PECVD chamber at a low pressure of 0.1 torr to 1.2 torr and a temperature of 300° C. to 500° C. and applying an RF power of 10 to 500 watt.
 11. The method according to claim 3, wherein the rapid thermal process step is carried out for an annealing period of 60 to 180 seconds at a temperature 700° C. to 850° C. in a chamber supplied with NH₃ gas in a flow rate of 1 to 10 slm.
 12. The method according to claim 1, wherein the forming the Al₂O₃ film step is carried out by depositing an Al₂O₃ film using a raw material of (CH₃)₃Al as a precursor in a chamber, kept at a temperature of 200° C. to 450° C. and a pressure of 0.1 torr to 1 torr while supplying H₂O gas.
 13. The method according to claim 6, wherein the furnace vacuum thermal treatment step is carried out using N₂ gas under the processing conditions of an annealing period of 5 to 60 minutes and a temperature or 600° C. to 850° C.
 14. The method according to claim 1, wherein as the upper electrode, a polysilicon film is deposited to a thickness of 1,000 Å.
 15. The method according to claim 1, wherein the lower electrode is formed of a polysilicon film.
 16. A method for manufacturing a capacitor in a semiconductor device, comprising: forming a nitride film over a lower electrode, which is on a semiconductor substrate, by using plasma; forming an amorphous TaON thin film over the nitride film; subjecting the amorphous TaON thin film to an RTA (Rapid Thermal annealing) treatment; forming an Al₂O₃ film over the amorphous TaOn thin film; subjecting the Al₂O₃ film to a furnace vacuum thermal treatment; and forming a polysilicon film over the Al₂O₃ film to form an upper electrode.
 17. The method according to claim 16, wherein the lower electrode has one of a cylindrical structure and a stacked structure.
 18. The method according to claim 16, wherein the forming the nitride film step forms the nitrude film over the lower electrode by conducting a plasma treatment in a chamber, kept at a pressure of 0.1 torr to 1.2 torr and a semiconductor substrate temperature of 300° C. to 500° C. for 10 to 600 seconds while supplying NH₃ gas in an amount of 10 to 500 sccm and applying an RF power of 10 to 500 watts.
 19. The method according to claim 16, wherein the forming the TaON film step forms an amorphous TaON thin film according to a PECVD (Plasma Enhanced Chemical Vapor Deposition) process by evaporating 0.001 cc to 2 cc of tantalum ethylate (Ta(OC₂H₅)₅) as a raw material in a vaporizer, kept at 170° C. to 190° C., to produce Ta chemical vapor, and supplying the Ta chemical vapor to the PECVD chamber, to which NH₃ gas is supplied in a flow rate of 10 to 500 sccm, while maintaining the PECVD chamber at a low pressure of 0.1 torr to 1.2 torr and a temperature of 300° C. to 500° C. and applying an RF power of 10 to 500 watt.
 20. The method according to claim 16, wherein the rapid thermal process step is carried out for an annealing period of 60 to 180 seconds at a temperature 700° C. to 850° C. in a chamber supplied with NH₃ gas in a flow rate of 1 to 10 slm
 21. The method according to claim 16, wherein the forming the Al₂O₃ film step is carried out by depositing an Al₂O₃ film using a raw material of (CH₃)₃Al as a precursor in a chamber, kept at a temperature of 200° C. to 450° C. and a pressure of 0.1 torr to 1 torr while supplying H₂O gas.
 22. The method according to claim 16, wherein the furnace vacuum thermal treatment step is carried out using N₂ gas under the processing conditions of an annealing period of 5 to 60 minutes and a temperature or 600° C. to 850° C.
 23. The method according to claim 16, wherein as the upper electrode, a polysilicon film is deposited to a thickness of 1,000 Å.
 24. A method of manufacturing a capacitor in a semiconductor substrate, comprising: forming a nitride film over a lower electrode on a semiconductor substrate; forming a TaON film over the nitride film; forming a non-titanium based contact layer on the TaON film; and forming an upper electrode over the non-titanium based contact layer. 